Your article is protected by copyright and all rights are held exclusively by Springer-Verlag GmbH Germany, part of Springer Nature. This e-offprint is for personal use only and shall not be self-archived in electronic repositories. If you wish to self-archive your article, please use the accepted manuscript version for posting on your own website. You may further deposit the accepted manuscript version in any repository, provided it is only made publicly available 12 months after official publication or later and provided acknowledgement is given to the original source of publication and a link is inserted to the published article on Springer's website. The link must be accompanied by the following text: "The final publication is available at link.springer.com".

This paper reports the inhibition efficiency of combinations of amine-terminated polyaminoamide (PAMAM) dendrimers of generation 1 and 2 and anionic polyelectrolytes in colloidal silica particle growth. The polyelectrolytes studied were PAA ) polyacrylate (low MW is 2 KDa, high MW is 450 KDa), PAM-co-AA ) poly(acrylamide-co-acrylate) of MW 200 KDa, CMI ) carboxymethylinulin (proprietary MW, between 2 and 3 KDa). The principle findings are summarized as follows: PAMAM-1 and -2 dendrimers are effective inhibitors of silica growth at 40 ppm dosage levels. The effect of anionic polycarboxylates on the inhibitory activity of PAMAM-1 and PAMAM-2 is dosagedependent. They do not affect PAMAM-1 inhibitory activity; they increase that of PAMAM-2 at low dosage (20 ppm) but exhibit detrimental effects at high dosage (>40 ppm), with CMI exerting no adverse effects at any dosage. (3) Negative charge density on the polymer is directly proportional to inhibitor activity deterioration. (4) Addition of polymer prevents dendrimer entrapment into the silica colloidal matrix by preventing formation of SiO 2 -dendrimer precipitates. This research was inspired by the recognition that diatom biosilica-associated peptides (silaffins natSil-1 and natSil-2) and long-chain polyamines (LCPA) profoundly influence silica formation from a silicic acid solution in vitro.

This paper reports the inhibition efficiency of a family of polyaminoamide (PAMAM) STARBURST ® dendrimers in colloidal SiO 2 growth. PAMAMs of various generations (0.5, 1.5, 2.5 with -COOH termini, and 1, and 2 with -NH 2 termini) were tested and compared to control samples. Superiority of the dendrimer inhibitors with -NH 2 termini (maintaining ∼380 ppm soluble SiO 2 after 12 h) versus those with -COOH termini (maintaining ∼180 ppm soluble SiO 2 after 12 h) was discovered in solutions containing 500 ppm initial SiO 2 . These inhibitors present potential for water treatment applications.